| - Accelerator solution for the application of REMA TIP TOP RAD, PN and UP repair patches, MINICOMBI, REMA STEM, SV bonding rubber, SEALASTIC, VULC COMPOUND
- SPECIAL CEMENT BL can be used for self-vulcanization starting from 18 °C (65 °F) through to hot vulcanization up to 150 °C (300 °F)
|
|
|
| - This accelerator solution dries twice as fast as the normal SPECIAL CEMENT BL
- Especially suitable for fast and smaller repairs such as to tread-area punctures and for larger one-step repairs with REMA TIP TOP RAD, PN and UP repair patches
- Can be used for self-vulcanization from 18 °C (65 °F) through to hot vulcanization at 150 °C (300 °F)
- Transparent and easy to distinguish from the standard SPECIAL CEMENT BL; used in the same way
|
|
|
| - Accelerator solution for coating the buffed tyre inside during the application of RADIAL, PN, or UP repair patches, with the vulcanizing temperature being higher than 85 °C (185 °F)
- HR Solution helps to extend the waiting time until the start of the curing process to a maximum of 14 days
|
|
|
| - Sealing porous innerliners and edges of repair areas
- Coating excessively buffed repair areas on the tyre inside
|
|
|
| - Accelerator solution for coating the buffed tyre inside, the buffed skive surface or the bonding layer of REMA TIP TOP repair patches prior to laminating with MTR RUBBER
- Thermopress MTR-Solution is adapted to MTR RUBBER with regard to its accelerator and adhesion system and can therefore be used at curing temperatures of at least 100 °C (212 °F)
|
|
|
| - T2-Solution is used for pre-treatment of the buffed skive before it is filled with T2-Compound
- The two components (A and B) are mixed in equal quantities in the amount required for the rubber surface
|